Methods for using bi-modal abrasive slurries for mechanical and chemical-mechanical planarization of microelectronic-device substrate assemblies

ABSTRACT

A method and apparatus for making and using slurries for planarizing microelectronic-device substrate assemblies in mechanical and/or chemical-mechanical planarization processes. In one aspect of the invention, a bi-modal slurry is fabricated by removing a first type of selected abrasive particles from a first abrasive particle solution to form a treated flow of the first solution. The treated flow of the first solution is then combined with a flow of a second solution having a plurality of second abrasive particles. The abrasive particles of the first type are accordingly removed from the first solution separately from the second solution such that the second abrasive particles in the second solution do not affect the removal of the abrasive particles of the first type from the first solution. In another aspect of the invention, a second type of selected abrasive particles are removed from the second solution prior to mixing with the first solution. Thus, by combining the treated flow of the first solution with either the treated or untreated flow of the second solution, a single flow of an abrasive slurry is produced having a first distribution of the first abrasive particles about a first mode and a second distribution of the second abrasive particles about a second mode.

TECHNICAL FIELD

[0001] The present invention relates to bi-modal slurries for planarizing microelectronic-device substrate assemblies, and to methods and apparatuses for making and using such slurries in mechanical and/or chemical-mechanical planarization processes.

BACKGROUND OF THE INVENTION

[0002] Mechanical and chemical-mechanical planarizing processes (collectively “CMP”) are used in the manufacturing of microelectronic devices for forming a flat surface on semiconductor wafers, field emission displays and many other microelectronic-device substrate assemblies. CMP processes generally remove material from a substrate assembly to create a highly planar surface at a precise elevation in the layers of material on the substrate assembly.

[0003]FIG. 1 schematically illustrates an existing web-format planarizing machine 10 for planarizing a substrate assembly 12. The planarizing machine 10 has a support table 14 with a top panel 16 at a workstation where an operative portion (A) of a polishing pad 40 is positioned. The top panel 16 is generally a rigid plate to provide a flat, solid surface to support the operative section of the polishing pad 40 during planarization.

[0004] The planarizing machine 10 also has a plurality of rollers to guide, position and hold the polishing pad 40 over the top panel 16. The rollers include a supply roller 20, first and second idler rollers 21 a and 21 b, first and second guide rollers 22 a and 22 b, and a take-up roller 23. The supply roller 20 carries an unused or preoperative portion of the polishing pad 40, and the take-up roller 23 carries a used or post-operative portion of the polishing pad 40. Additionally, the first idler roller 21 a and the first guide roller 22 a stretch the polishing pad 40 over the top panel 16 to hold the polishing pad 40 stationary during operation. A drive motor (not shown) drives at least one of the supply roller 20 and the take-up roller 23 to sequentially advance the polishing pad 40 across the top panel 16. As such, clean preoperative sections of the polishing pad 40 may be quickly substituted for used sections to provide a consistent surface for planarizing the substrate assembly 12.

[0005] The web-format planarizing machine 10 also has a carrier assembly 30 that controls and protects the substrate assembly 12 during planarization. The carrier assembly 30 generally has a carrier head 31 with a plurality of vacuum holes 32 to pick up and release the substrate assembly 12 at appropriate stages of the planarizing cycle. A plurality of nozzles 41 attached to the carrier head 31 dispense a planarizing solution 42 onto a planarizing surface 43 of the polishing pad 40. The carrier assembly 30 also generally has a support gantry 34 carrying a drive assembly 35 that translates along the gantry 34. The drive assembly 35 generally has actuator 36, a drive shaft 37 coupled to the actuator 36, and an arm 38 projecting from the drive shaft 37. The arm 38 carries the carrier head 31 via another shaft 39 such that the drive assembly 35 orbits the carrier head 31 about an axis B-B offset from a center point C-C of the substrate assembly 12.

[0006] The polishing pad 40 and the planarizing solution 42 define a planarizing medium that mechanically and/or chemically-mechanically removes material from the surface of the substrate assembly 12. The web-format planarizing machine 10 typically uses a fixed-abrasive polishing pad having a plurality of abrasive particles fixedly bonded to a suspension material. The planarizing solutions 42 used with fixed-abrasive pads are generally “clean solutions” without abrasive particles because the abrasive particles in conventional abrasive CMP slurries may ruin the abrasive surface of fixed-abrasive pads. In other applications, the polishing pad 40 may be a nonabrasive pad composed of a polymeric material (e.g., polyurethane), a resin, or other suitable materials without abrasive particles. The planarizing solutions 42 used with nonabrasive polishing pads are typically “abrasive” CMP slurries with abrasive particles.

[0007] To planarize the substrate assembly 12 with the planarizing machine 10, the carrier assembly 30 presses the substrate assembly 12 against the planarizing surface 43 of the polishing pad 40 in the presence of the planarizing solution 42. The drive assembly 35 then orbits the carrier head 31 about the offset axis B-B to translate the substrate assembly 12 across the planarizing surface 43. As a result, the abrasive particles and/or the chemicals in the planarizing medium remove material from the surface of the substrate assembly 12.

[0008] CMP processes should consistently and accurately produce a uniformly planar surface on the substrate assembly 12 to enable precise fabrication of circuits and photo-patterns. For example, during the fabrication of transistors, contacts, interconnects and other components, many substrate assemblies develop large “step heights” that create a highly topographic surface across the substrate assembly 12. To enable the fabrication of integrated circuits with high densities of components, it is necessary to produce a highly planar substrate surface at several stages of processing the substrate assembly 12 because non-planar substrate surfaces significantly increase the difficulty of forming submicron features. For example, it is difficult to accurately focus photo-patterns to within tolerances of 0.1 pun on nonplanar substrate surfaces because submicron photolithographic equipment generally has a very limited depth of field. Thus, CMP processes are often used to transform a topographical substrate surface into a highly uniform, planar substrate surface.

[0009] In the competitive semiconductor industry, it is also highly desirable to have a high yield of operable devices after CMP processing by quickly producing a uniformly planar surface at a desired endpoint on a substrate assembly. For example, when a conductive layer on the substrate assembly 12 is under-planarized in the formation of contacts or interconnects, many of these components may not be electrically isolated from one another because undesirable portions of the conductive layer may remain on the substrate assembly 12. Additionally, when a substrate assembly 12 is over-planarized, components below the desired endpoint may be damaged or completely destroyed. Thus, to provide a high yield of operable microelectronic devices, CMP processing should quickly remove material until the desired endpoint is reached.

[0010] To accurately create highly planar substrate surfaces at the desired endpoint, the particle size distribution of planarizing slurries should be consistent from one planarizing cycle to another. One problem with CMP processing, however, is that the abrasive particles may be unstable in the slurry. For example, because many types of abrasive particles have a large affinity for one another, individual particles in a liquid solution may agglomerate into larger abrasive elements. The formation of such abrasive elements affects the consistency of the slurry because the extent that the particles agglomerate varies from one batch of slurry to another, or even within a single batch of slurry as it is delivered to the planarizing machine. Additionally, large abrasive elements may scratch the substrate assemblies and produce defects, or they may settle out of the solution. Thus, the agglomeration of abrasive particles is a serious problem for processing substrate assemblies with CMP processing.

[0011] One particularly promising CMP slurry being developed by Micron Technology, Inc. is a liquid solution having a plurality of first and second abrasive particles. The first and second abrasive particles are typically composed of the same material, such as ceria or silica treated ceria abrasive particles. The difference between the first and second abrasive particles is the size of the particles. This slurry accordingly has a “bi-modal” distribution of abrasive particles in which the first abrasive particles have particles sizes in a first size distribution about a first mode and the second abrasive particles have particle sizes in a second size distribution about a second mode. In contrast to “singlets slurries that have only one mode and a signal size distribution of abrasive particles about that mode, bi-modal slurries are expected to exhibit unusually good polishing rates and planarity on both topographical and planar substrate surfaces.

[0012] Although bi-modal slurries can produce good results, they may fail to achieve consistent results because the abrasive particles are highly unstable in the solution. The bi-modal slurries mixed by Micron Technology Inc. from components supplied by Rodel Corporation may even change from one planarizing cycle to the next, which greatly increases the difficulty in accurately planarizing substrate assemblies. To resolve the instability of these slurries, a point-of-use filtering may be performed at the planarizing machine of a single flow of a bi-modal slurry having both the first and second planarizing particles. Filtering the bi-modal slurry, however, may alter the bi-modal distribution of abrasive particles to the extent that the bi-modal slurry loses at least some of the advantages of using two different particle sizes. Therefore, there is a need for improved bi-modal slurry techniques in CMP processing to achieve the potential advantages of such slurries.

SUMMARY OF THE INVENTION

[0013] The present invention is directed toward methods and apparatuses for making and using slurries for planarizing microelectronic-device substrate assemblies in mechanical and/or chemical-mechanical planarization processes. In one aspect of the invention, a bi-modal slurry is fabricated by removing a first type of selected abrasive particles from a first abrasive particle solution to form a treated flow of the first solution. The treated flow of the first solution is then combined with a flow of a second solution having a plurality of second abrasive particles. A single flow of an abrasive slurry thus has a first distribution of the first abrasive particles and a second distribution of the second abrasive particles.

[0014] In another aspect of the invention, a bi-modal abrasive slurry is manufactured by also separating a second type of selected abrasive particles from the second solution prior to combining the first solution with the second solution. Thus, the first and second solutions can be treated independently to avoid affecting the treatment of one solution by treating the other solution.

[0015] In still another aspect of the invention, a planarizing apparatus for planarizing a substrate assembly in accordance with the invention includes a slurry manufacturing assembly, and a dispenser coupled to the slurry manufacturing assembly. The slurry manufacturing assembly can include a first feed line for containing the first flow of the first solution having the plurality of the first abrasive particles, a second feed line for containing the second flow of the second solution having the plurality of second abrasive particles, a first filter coupled to the first feed line to filter the plurality of the first abrasive particles separately from the second flow of the second solution, and a combined feed line operatively coupled to the first filter and the second feed line for containing a combined flow of the first and second solutions after filtering the first solution.

BRIEF DESCRIPTION OF THE DRAWINGS

[0016]FIG. 1 is a schematic cross-sectional view of a planarizing machine in accordance with the prior art.

[0017]FIG. 2 is a schematic side view of a planarizing system including a planarizing machine and a slurry manufacturing assembly in accordance with one embodiment of the invention.

[0018]FIG. 3 is a block diagram illustrating first and second slurry solutions being processed according to a method for making a planarizing solution in accordance with an embodiment of the invention.

[0019]FIG. 4 is a bar graph illustrating a slurry made using a slurry manufacturing assembly and method in accordance with one embodiment of the invention having a bi-modal particle size distribution including a first size distribution of first abrasive particles about a first mode and a second size distribution of smaller second abrasive particles about a second mode.

[0020]FIG. 5 is a schematic side view of a planarizing system including a planarizing machine and a slurry manufacturing assembly in accordance with another embodiment of the invention.

DETAILED DESCRIPTION OF THE INVENTION

[0021] The present invention is directed to methods and apparatuses for making and using slurries for planarizing microelectronic-device substrate assemblies in mechanical and/or chemical-mechanical planarization processes. Many specific details of certain embodiments of the invention are set forth in FIGS. 2-5 and the following description to provide a thorough understanding of such embodiments. One skilled in the art, however, will understand that the present invention may have additional embodiments, or that certain embodiments of the invention may be practiced without several of the details described in the following description.

[0022]FIG. 2 is a schematic side view illustrating a planarizing system 100 having a planarizing machine 110 and a slurry manufacturing assembly 200 in accordance with one embodiment of the invention. The planarizing machine 110 shown in FIG. 2 is similar to the web-format planarizing machine 10 described above with reference to FIG. 1, and thus like reference numbers refer to like parts. The planarizing machine 110 can also be a rotary planarizing machine having a rotating platen and a circular polishing pad, as set forth in U.S. Pat. Nos. 5,645,682 and 5,792,709, which are both herein incorporated by reference. Suitable web-format planarizing machines without the slurry manufacturing assembly 200 are manufactured by Obsidian Corporation. Suitable rotary planarizing machines without the slurry manufacturing assembly 200 are manufactured by Westech Corporation and Strasbaugh Corporation.

[0023] The slurry manufacturing assembly 200 generally includes a first supply container 210 containing a first solution 212 and a second supply container 220 containing a second solution 222. In this particular embodiment, the slurry manufacturing assembly 200 also includes a first particle removal unit 230 coupled to the first container 210, a second particle removal unit 235 coupled to the second container 220, and a mixing unit 240 coupled to the first and second particle removal units 230 and 235. As explained below, the first and second particle removal units 230 and 235 are preferably first and second filtration units that separately filter selected abrasive particles from the first and second solutions 212 and 222. The filtered first and second solutions 212 and 222 are then combined in the mixing unit 240 to form an abrasive slurry 242 for planarizing the substrate assembly 12 on the planarizing machine 110.

[0024] The first solution 212 is a first slurry component of the abrasive slurry 242. The first solution 212 preferably includes water, chemical additives (e.g., dispersants, surfactants, oxidants and other additives), and a plurality of first abrasive particles 216. The first abrasive particles 216 can be aluminum oxide particles, ceria particles, silicon dioxide particles, titanium oxide particles, tantalum oxide particles, ceria treated silica particles, or other suitable abrasive particles for removing material from microelectronic device substrate assemblies. The first abrasive particles 216 are preferably the larger particles of a bi-modal abrasive slurry having particle sizes from approximately 0.070-1.0 μm, and more preferably from approximately 0.070-0.40 μm. When the first solution 212 is in the first container 210 prior to being mixed with the second solution 222, a significant percentage of the first abrasive particles 216 in the first solution 212 may agglomerate to form first particle agglomerations 218. Each first particle agglomeration 218 may accordingly include two or more individual abrasive particles 216. The individual abrasive particles 216 of the first particle agglomerations 218 are generally bonded together electronically, covalently, or by van der walls interaction.

[0025] The second solution 222 is accordingly a second component of the mixed slurry 242. The second solution 222 generally includes a liquid 224, the same additives that are in the first solution 212, and a plurality of second abrasive particles 226. The second abrasive particles 226 can also be composed of the same material as the first abrasive particles 216 in the first solution 212, such as aluminum oxide particles, ceria particles, silicon dioxide particles, titanium oxide particles, tantalum oxide particles, ceria treated silica particles, or other suitable abrasive particles for removing material from microelectronic device substrate assemblies. The second abrasive particles 226 are preferably the smaller particles of a bi-modal abrasive slurry having particle sizes from approximately 0.005-0.20 μm, and more preferably from approximately 0.010-0.050 μm. As with the first solution 212, many of the abrasive particles 226 in the second solution 222 may agglomerate into second particle agglomerations” 228.

[0026] The first particle removal unit 230 of this embodiment is coupled to a first feed line 219 (indicated by reference numbers 219 a and 219 b) between the first container 210 and the mixing unit 240. The first particle removal unit 230 removes a first type of selected abrasive particles from the first solution 212. The first particle removal unit 230, for example, can have a filter 232 that removes large individual abrasive particles 216 and first particle agglomerations 218 having sizes greater than a first maximum particle size for the first abrasive particles. For example, to create a first particle size distribution from approximately 0.070-1.0 μm, the first particle removal unit 230 removes first abrasive particles 216 and particle agglomerations 218 having sizes greater than 1.0 μm. Similarly, to create a first particle size distribution from approximately 0.070-0.40 μm, the first particle removal unit 230 removes first abrasive particles 216 and particle agglomerations 218 having sizes greater than 0.40 μm. Suitable filters for removing the first type of selected abrasive particles from the first solution 212 are manufactured by Millipore Corporation.

[0027] The second particle removal unit 235 of this embodiment is coupled to a feed line 229 (indicated by reference numbers 229 a and 229 b) between the second container 220 and the mixing unit 240. The second particle removal unit 235 removes a second type of abrasive particles from the second solution 222. The second particle removal unit 235 can also have a filter 237 that removes large second abrasive particles 226 and second particle agglomerations 228 having sizes greater than a second maximum particle size. For example, to create a second particle size distribution from approximately 0-010-0.20 μm, the second particle removal unit 235 removes second abrasive particles 226 and particle agglomerations 228 having sizes greater than 0.20 μm. Similarly, to create a second particle size distribution from approximately 0.010-0.050 μm, the second particle removal unit 235 removes second abrasive particles 226 and particle agglomerations 228 having sizes greater than 0.050 μm. Suitable filters for removing the second type of selected abrasive particles from the second abrasive particles 226 are also manufactured by Millipore Corporation.

[0028]FIG. 3 is a schematic view illustrating the operation of the embodiment of the slurry manufacturing assembly 200 shown in FIG. 2. Referring to FIGS. 2 and 3 together, an untreated flow of the first solution 212 initially flows to the first particle removal unit 230 through a first segment of the first feed line 219 a, and an untreated flow of the second solution 222 initially flows to the second particle removal unit 235 through a first segment of the second feed line 229 a. The first particle removal unit 230 passes the untreated flow of the first solution 212 through the filter 232 to remove large individual first abrasive particles 216 a and large first particle agglomerations 218 from the first solution 212. A treated portion of the first solution 212 then passes from the first particle removal unit 230 through a second segment of the first feed line 219 b and into the mixing unit 240. The second particle removal unit 235 separately passes the untreated flow of the second solution 222 through the filter 237 to remove the large individual abrasive particles 226 and second particle agglomerations 228 from the untreated second solution 222 to create a treated flow of the second solution 222. The second particle removal unit 235 then passes the treated flow of the second solution 222 through a second segment of the second feed line 229 b and into the mixing unit 240.

[0029] The mixing unit 240 then mixes the treated first and second solutions 212 and 222 together by using an agitator 241, turbulence within a conduit, and/or other suitable devices for adequately mixing the first and second solutions 212 and 222. The combination of the first and second solutions 212 and 222 forms an abrasive slurry 242 with a first particle size distribution of larger first abrasive particles 216 about a first mode and a second particle size distribution of smaller second abrasive particles 226 about a second mode.

[0030]FIG. 4 is a bar graph illustrating a bi-modal particle size distribution of the planarizing slurry 242 having a first particle size distribution 280 from approximately 0.20-1.0 μm of the larger first abrasive particles 216 (FIG. 2) and a second particle size distribution 290 from approximately 0.020-0.20 μm of the smaller second abrasive particles 226 (FIG. 2). The first particle size distribution 280 has a first mode 282 identifying that a significant percentage of the first abrasive particles 216 have particle sizes of approximately 0.3-0.4 μm. The second particle size distribution 290 has a second mode 292 identifying that a significant percentage of the second abrasive particles 226 have particle sizes of approximately 0.07-014 μm. In another embodiment (not shown), the first particle size distribution is from approximately 0.070-0.400 μm with a first mode at approximately 0.250-0.300 μm, and the second particle size distribution is from approximately 0.010-0.050 μm with a second mode at approximately 0.020-0.030 μm.

[0031] The embodiment of the slurry manufacturing assembly 200 and the method of manufacturing the slurry 242 described above with reference to FIGS. 2 and 3 are expected to produce bi-modal planarizing slurries with consistent first and second particle size distributions. One aspect of the embodiment of FIGS. 2-4 is the discovery that conventional filtering processes for a bi-modal slurry produce inconsistent particle size distributions because the filters remove a disproportionate percentage of the larger first abrasive particles after operating for a period of time. This phenomenon may occur because a common filter sized to remove the upper end of the larger particles is generally too large to also remove agglomerations of the smaller particles. Moreover, as the filter becomes loaded with abrasive particles, the removal rate of larger abrasive particles increases without necessarily increasing the removal rate of the smaller second abrasive particles. The slurry manufacturing system 200 and the methods for making the slurry 242 reduce variations in the first and second particle size distributions because the first and second solutions 212 and 222 are filtered separately to provide more consistent filtering of the individual solutions. The slurry manufacturing system 200 is accordingly expected to have less loading of the filters in a manner that removes a disproportionate percentage of the first abrasive particles 216 from the planarizing solution 242. Thus, the manufacturing system 200 and the methods for manufacturing the planarizing slurry 242 are expected to provide more consistent first and second particle size distributions in a bi-modal slurry.

[0032] The bi-modal slurry 242 manufactured in accordance with the method described above with reference to FIGS. 2 and 3 is also expected to produce good planarizing results. Small abrasive particles are expected to planarize highly topographic surfaces much faster than large abrasive particles. Once the surface of the substrate assembly becomes planar, however, slurries with small particles may have a much slower removal rate than slurries with large particles. The bi-modal planarizing solution 242 manufactured in accordance with the embodiment of FIGS. 2-4 includes the small second abrasive particles 226 to provide selective removal of high areas on the substrate surface at an initial stage of a planarizing cycle while the substrate surface has topographical variations. The bi-modal slurry 242 also includes the larger first abrasive particles 216 for maintaining a high removal rate once the substrate surface becomes planar. The planarizing solution 242 accordingly provides selective removal of the topographical features to form a planar surface on the substrate assembly, and then maintains a high removal rate of material from the blanket surface to expediently planarize the substrate assemblies.

[0033]FIG. 5 is a schematic view illustrating a planarizing system 100 a having the planarizing machine 110 and a slurry manufacturing assembly 200 a in accordance with another embodiment of the invention. In this embodiment, the slurry manufacturing assembly 200 a has the first supply container 210 containing the first solution 212, the second supply container 220 containing the second solution 222, and only the first particle removal unit 230 coupled to the first container 210 and the mixing unit 240. The slurry manufacturing assembly 200 a accordingly only treats the flow of the first solution 212 to filter or otherwise remove the first type of selected abrasive particles from the first abrasive particles 216. The planarizing system 100 a is otherwise expected to operate in a manner similar to the planarizing system 100 described above.

[0034] Referring to FIG. 2 or FIG. 5, the substrate 12 is planarized by fabricating the mixed slurry 242 and then depositing the mixed slurry 242 onto the polishing pad 40 via the nozzles 41 on the carrier head 31. As the mixed slurry 242 covers the polishing pad 40, the carrier assembly 30 presses the substrate 12 against the planarizing surface 43 of the pad 40 and translates the substrate 12 across the planarizing surface 43. Because the slurry manufacturing assemblies 200 and 200 a produce slurries with consistent first and second particle size distributions, the planarizing systems 100 and 100 a are expected to consistently produce highly planar and substantially defect free surfaces on the finished substrate assemblies 12.

[0035] From the foregoing it will be appreciated that, although specific embodiments of the invention have been described herein for purposes of illustration, various modifications may be made without deviating from the spirit and scope of the invention. Accordingly, the invention is not limited except as by the appended claims. 

1-30. (Cancelled)
 31. In the manufacturing of microelectronic devices, a method of planarizing microelectronic-device substrate assemblies, comprising: fabricating an abrasive slurry by filtering a first solution having a plurality of first abrasive particles to create a filtered flow of the first solution, generating a flow of a second solution having a plurality of second abrasive particles separately from filtering the first solution, the second abrasive particles being different from the first abrasive particles in the filtered flow of the first solution, and combining the filtered flow of the first solution and the flow of the second solution into a single abrasive slurry having a first distribution of the first abrasive particles and a second distribution of the second abrasive particles; dispensing the abrasive slurry onto a planarizing surface of a polishing pad; and removing material from a substrate assembly by pressing the substrate assembly against the planarizing surface and moving at least one of the substrate assembly and the polishing pad with respect to the other to translate the substrate assembly across the planarizing surface. 32-37. (Cancelled)
 38. In the manufacturing of microelectronic devices, a method of planarizing microelectronic-device substrate assemblies, comprising: fabricating an abrasive slurry by removing a first type of selected abrasive particles from a plurality of first abrasive particles in a first solution to create a treated flow of the first solution, generating a second flow of a second solution having a plurality of second abrasive particles, the second abrasive particles being different from the first abrasive particles in the treated flow of the first solution and combining the treated flow of the first solution and the flow of the second solution to create a single flow of an abrasive slurry having the first abrasive particles and the second abrasive particles; dispensing the abrasive slurry onto a planarizing surface of a polishing pad; and removing material from a substrate assembly by pressing the substrate assembly against the planarizing surface and moving at least one of the substrate assembly and the polishing pad with respect to the other to translate the substrate assembly across the planarizing surface. 39-74. (Cancelled)
 75. The method of claim 31 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein creating the filtered flow of the fist solution comprises selectively capturing the first type of selected abrasive particles from an untreated flow of the first solution.
 76. The method of claim 31 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein creating the filtered flow of the fist solution comprises filtering an untreated flow of the first solution through a filter that removes first abrasive particles having particle sizes greater than a maximum desired particle size for the first abrasive particles.
 77. The method of claim 76 wherein filtering the first solution comprises passing the first solution through a first filter that removes first abrasive particles from the first solution having particles sizes greater than the maximum desired particle size for the first abrasive particles.
 78. The method of claim 77 wherein passing the first solution through a first filter comprises driving a flow of the first solution through a filter that removes particles having sizes greater than approximately 0.8 μm. 79 The method of claim 77 wherein passing the first solution through a first filter comprises driving a flow of the first solution through a filter that removes particles having sizes greater than approximately 0.3 μm.
 80. The method of claim 31 wherein prior to combining the first filtered flow of the first solution with the flow of the second solution, the method further comprises separating a second type of selected abrasive particles from the second abrasive particles of the second solution to create a treated flow of the second solution, the filtered flow of the second solution being combined with the filtered flow of the first solution to create the single flow of the abrasive slurry.
 81. The method of claim 80 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein separating the second type of selected abrasive particles from the plurality of the second abrasive particles comprises selectively capturing the second type of selected abrasive particles from an untreated flow of the second solution.
 82. The method of claim 81 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein separating the second type of selected abrasive particles from the plurality of the second abrasive particles comprises filtering a flow of the second solution through a filter that removes second abrasive particles having particle sizes greater than a maximum desired particle size for the second abrasive particles.
 83. The method of claim 82 wherein filtering the second solution comprises passing the second solution through a second filter that removes second abrasive particles from the second solution having particles sizes greater than the maximum desired particle size for the second abrasive particles.
 84. The method of claim 83 wherein passing the second solution through a second filter comprises driving a flow of the second solution through a filter that removes particles having sizes greater than approximately 0.15 μm.
 85. The method of claim 83 wherein passing the second solution through a second filter comprises driving a flow of the second solution through a filter that removes particles having sizes greater than 0.050 μm.
 86. The method of claim 31 wherein combining the first solution with the second solution comprises actively agitating the treated first solution and the second solution in a mixing unit.
 87. The method of claim 31 wherein combining the first filtered flow of the first solution with the flow of the second solution comprises passing the combined filtered first solution and second solution through a turbulent zone of a conduit. 88 The method of claim 31 wherein combining the filtered flow of the first solution with the second solution comprises mixing 1-99% by volume of the first filtered solution with 1-99% by volume of the second solution.
 89. The method of claim 88 wherein mixing the first filtered solution with the second solution comprises altering a mix ratio of the first filtered solution and second solution during a single polishing cycle.
 90. The method of claim 89 wherein altering the mix ratio comprises changing from a first mix ratio of the first filtered solution and second solution to a second mix ratio of the first filtered solution and the second solution.
 91. The method of claim 38 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein removing the first type of abrasive particles from the plurality of the first abrasive particles comprises selectively capturing the first type of selected abrasive particles from an untreated flow of the first solution.
 92. The method of claim 38 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein removing the first type of abrasive particles from the plurality of the first abrasive particles comprises filtering an untreated flow of the first solution through a filter that removes first abrasive particles having particle sizes greater than a maximum desired particle size for the first abrasive particles.
 93. The method of claim 92 wherein filtering the first solution comprises passing the first solution through a first filter that removes first abrasive particles from the first solution having particles sizes greater than the maximum desired particle size for the first abrasive particles.
 94. The method of claim 93 wherein passing the first solution through a first filter comprises driving a flow of the first solution through a filter that removes particles having sizes greater than approximately 0.8 μm.
 95. The method of claim 93 wherein passing the first solution through a first filter comprises driving a flow of the first solution through a filter that removes particles having sizes greater than approximately 0.3 μm.
 96. The method of claim 38 wherein prior to combining the treated flow of the first solution with the flow of the second solution, the method further comprises separating a second type of selected abrasive particles from the second abrasive particles of the second solution to create a treated flow of the second solution, the treated flow of the second solution being combined with the treated flow of the first solution to create the single flow of the abrasive slurry.
 97. The method of claim 96 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein separating the second type of selected abrasive particles from the plurality of the second abrasive particles comprises selectively capturing the second type of selected abrasive particles from an untreated flow of the second solution.
 98. The method of claim 97 wherein the first abrasive particles have a first size distribution with a first mean and the second abrasive particles have a second size distribution with a second mean smaller than the first mean of the first size distribution, and wherein separating the second type of selected abrasive particles from the plurality of the second abrasive particles comprises filtering a flow of the second solution through a filter that removes second abrasive particles having particle sizes greater than a maximum desired particle size for the second abrasive particles.
 100. The method of claim 99 wherein filtering the second solution comprises passing the second solution through a second filter that removes second abrasive particles from the second solution having particles sizes greater than the maximum desired particle size for the second abrasive particles.
 101. The method of claim 100 wherein passing the second solution through a second filter comprises driving a flow of the second solution through a filter that removes particles having sizes greater than approximately 0.15 μm.
 102. The method of claim 100 wherein passing the second solution through a second filter comprises driving a flow of the second solution through a filter that removes particles having sizes greater than 0.050 μm.
 103. The method of claim 38 wherein combining the treated flow of the first solution with the second solution comprises actively agitating the treated first solution and the second solution in a mixing unit.
 104. The method of claim 38 wherein combining the treated flow of the first solution with the second solution comprises passing the combined treated first solution and second solution through a turbulent zone of a conduit.
 105. The method of claim 38 wherein combining the treated flow of the first and second solutions comprises mixing 1-99% by volume of the first solution with 1-99% by volume of the second solution.
 106. The method of claim 105 wherein mixing the treated flow of the first solution with the second solution comprises altering a mix ratio of the first and second solutions during a single polishing cycle.
 107. The method of claim 106 wherein altering the mix ratio comprises changing from a first mix ratio of the treated flow of the first solution and the second solution to a second mix ratio of the first and second solutions. 